Became an indispensable engineering material for aerospace, Marine, chemical and petrochemical industries.
Titanium ranks 9th among the elements that constitute the Earths crust.
In 1966, the United States listed titanium as the 9th industrial element.
Density of titanium: 4.51g/cm.
Weight：57% of steel.
3.5 times that of stainless steel.
1.3 times that of aluminum alloy.
1.7 times that of magnesium alloy.
Brand：TA1、TA2、TA3、TA4、TA5、GradesF1、GradesF2、GradesF3、GradesF4、GradesF5、Ti1、Ti2、Ti3、Ti4、Ti5
| Product | Specification | |
| mm | Inch | |
| Titanium Ingots | Φ360mm-Φ1020mm | (14.17-40.15Inch) |
| Titanium Plate |
80 mm x 1500mm x 2600mm
-
400mm x 1500mm x 2600mm
|
3.15 x 59 x 102 Inch.
-
15.7 x 59 x 102 Inch.
|
| Titanium Plate-Heat Forging |
3mm x 800mm x 6000mm
-
12mm x 1560mm x 6000mm
|
0.12 x 31.5 x 236 Inch.
-
0.47 x 61.5 x 236 Inch.
|
| Titanium Plate-Forging |
0.1mm x 350mm x Length
-
3.0mm x 1300mm x Length
|
0.00393 x 13.78 x Length Inch.
-
0.472 x 51.2 x Length Inch.
|
|
GB/T 39799-2024、GB/T 3620
ASTM B265、ASTM F136、ASTM F67、AMS4928
|
||
Titanium Sponge Production Process: Smelting by VAR and EB furnace in two ways
Titanium Ingot→ Forging → Plate → Rolling → Annealing → Titanium Coil → Strip → Testing→ packaging → Delivery.
Hot forging process: Performed above the recrystallization temperature of the metal.
| Chemical Composition | |||||||||||
| Grade | N | C | H | Fe | O | Al | V | Pa | Mo | Ni | Ti |
| Gr1 | 0.03 | 0.08 | 0.015 | 0.2 | 0.18 | / | / | / | / | / | bal |
| Gr2 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | / | / | / | bal |
| Gr3 | 0.05 | 0.08 | 0.015 | 0.3 | 0.35 | / | / | / | / | / | bal |
| Gr4 | 0.05 | 0.08 | 0.015 | 0.5 | 0.4 | / | / | / | / | / | bal |
| Gr5 | 0.05 | 0.08 | 0.015 | 0.4 | 0.2 |
5.5 ~ 6.75 |
3.5 ~ 4.5 |
/ | / | / | bal |
| Gr7 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / |
0.12 ~ 0.25 |
/ | / | bal |
| Gr9 | 0.03 | 0.08 | 0.015 | 0.25 | 0.15 |
2.5 ~ 3.5 |
2.0 ~ 3.0 |
/ | / | / | bal |
| Gr12 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | / |
0.2 ~ 0.4 |
0.6 ~ 0.9 |
bal |
Hot rolling:
Carried out at temperatures higher than recrystallization.
Cold rolling process:
Plastic deformation temperature is lower than the recovery temperature.
Annealing:
A metal heat treatment process in which the metal is slowly heated to a certain temperature, held for a sufficient time, and then cooled at a suitable rate.
Pickling:
The part is immersed in an aqueous solution such as sulfuric acid to remove the oxide film on the metal surface.
It is the pre-treatment or intermediate treatment of electroplating, enamel, rolling and other processes.