Density of titanium: 4.51g/cm.
Weight：57% of steel.
3.5 times that of stainless steel.
1.3 times that of aluminum alloy.
1.7 times that of magnesium alloy.
| Product | Specification | |
| mm | Inch | |
| Titanium Ingots | Φ360mm-Φ1020mm | (14.17-40.15Inch) |
| Titanium Plate |
80 mm x 1500mm x 2600mm
-
400mm x 1500mm x 2600mm
|
3.15 x 59 x 102 Inch.
-
15.7 x 59 x 102 Inch.
|
| Titanium Plate-Heat Forging |
3mm x 800mm x 6000mm
-
12mm x 1560mm x 6000mm
|
0.12 x 31.5 x 236 Inch.
-
0.47 x 61.5 x 236 Inch.
|
| Titanium Foil-Forging |
0.1mm x 350mm x Length
-
3.0mm x 1300mm x Length
|
0.00393 x 13.78 x Length Inch.
-
0.472 x 51.2 x Length Inch.
|
|
GB/T 39799-2024、GB/T 3620
ASTM B265、ASTM F136、ASTM F67、AMS4928
|
||
Titanium Sponge Production Process: Smelting by VAR and EB furnace in two ways
Titanium Ingot→ Forging → Plate → Rolling → Annealing → Titanium Coil → Strip → Testing→ packaging → Delivery
Hot forging process: Performed above the recrystallization temperature of the metal.
| Chemical Composition | |||||||||||
| Grade | N | C | H | Fe | O | Al | V | Pa | Mo | Ni | Ti |
| Gr1 | 0.03 | 0.08 | 0.015 | 0.2 | 0.18 | / | / | / | / | / | bal |
| Gr2 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | / | / | / | bal |
| Gr3 | 0.05 | 0.08 | 0.015 | 0.3 | 0.35 | / | / | / | / | / | bal |
| Gr4 | 0.05 | 0.08 | 0.015 | 0.5 | 0.4 | / | / | / | / | / | bal |
| Gr5 | 0.05 | 0.08 | 0.015 | 0.4 | 0.2 |
5.5 ~ 6.75 |
3.5 ~ 4.5 |
/ | / | / | bal |
| Gr7 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / |
0.12 ~ 0.25 |
/ | / | bal |
| Gr9 | 0.03 | 0.08 | 0.015 | 0.25 | 0.15 |
2.5 ~ 3.5 |
2.0 ~ 3.0 |
/ | / | / | bal |
| Gr12 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | / |
0.2 ~ 0.4 |
0.6 ~ 0.9 |
bal |
Hot rolling:
Carried out at temperatures higher than recrystallization.
Cold rolling process:
Plastic deformation temperature is lower than the recovery temperature.
Annealing:
A metal heat treatment process in which the metal is slowly heated to a certain temperature, held for a sufficient time, and then cooled at a suitable rate.
Pickling:
The part is immersed in an aqueous solution such as sulfuric acid to remove the oxide film on the metal surface.
It is the pre-treatment or intermediate treatment of electroplating, enamel, rolling and other processes